PA6.10 & PA6.12 Polymers
             
PRODUCT POLYAMIDE 6.10 POLYAMIDE 6.12
Type 7030 7050 8030 8070
Designation 134 SC 00 D 134 SC 00 PC223 134 DH 00 D 134 DH 00 PC220
   
General properties         Unit Method
Density 1.07 1.07 1.06 1.06 g/cm3 ISO 1183-1
Viscosity number, formic acid 90 % 138 223 138 220 ml/g ISO 307
Water absorption, saturation in water 23°C 2.00 2.00 2.00 2.00 % ISO 62
Moisture absorption, sat. in 23°C/50 % r.h. atm. 0.90 0.90 0.90 0.90 % ISO 62
Thermal properties            
Melting temperature, DSC 223 223 215 215 °C ISO 11357-1/-3
Solidification point 192 192 186 186 °C ISO 11357-1/-3
Mechanical properties    
  DAM Cond. DAM Cond. DAM Cond. DAM Cond. DAM - Dry As Moulded  
Tensile modulus Et 2,123 1,635 2,368 1,654 2,468 1,660 1,978 1,588 MPa ISO 527-2/1A/1
Yield stress σy 61.8 48.3 64.5 50.1 60.6 49.9 59.9 50.3 MPa ISO 527-2/1A/50
Yield strain εy 4.6 21.2 4.1 20.4 4.2 17.6 4.1 18.8 % ISO 527-2/1A/50
Nominal strain at break εtb 124 88 243 170 78 128 234 275 % ISO 527-2/1A/50
Flexural modulus Ef 2,022 1,458 2,208 1,549 2,088 1,615 2,138 1,623 MPa ISO 178
Flexural strength σfM 83.2 57.6 86.8 59.6 83.4 61.7 81.4 60.6 MPa ISO 178
Flexural strength σfC 65.3 43.4 70.3 45.3 67.7 48.3 67 47.7 MPa ISO 178
Charpy impact strength acU   23 °C
Charpy impact strength acU  -30 °C
No break
No break
No break
No break
No break
No break
No break
No break
No break
No break
No break
No break
No break
No break
No break
No break
kJ/m2
kJ/m2
ISO 179-1/1eU
Charpy notched impact strength acA     23 °C
Charpy notched impact strength acA    -30 °C
5.2
3.9
8.2
4.9
5.3
6.0
10.0
6.9
4.9
4.6
7.0
5.3
5.3
5.4
8.3
6.2
kJ/m2
kJ/m2
ISO 179-1/1eU
             
TYPE Viscosity number Moisture Content Chip Weight Chip Dimension Melting Point Solidification Point
(ml/g) (%) (mg) (mm) (°C) (°C)
PA 6.10 * Viscosity ISO-Std.307, VI (Formic Acid 90%)
7030 138 < 0,07 13 2.7 2.8 3.4 223 192
7035 154
7040 189
7050 223
7060 248
Under Development
7005 113 < 0,07 13 2.7 2.8 3.4 223 192
7011 125
PA 6.12 * Viscosity ISO-Std.307, VI (Sulfuric Acid 96%)
8030 138 < 0,07 13 2.7 2.8 3.4 215 186
8040 160
8050 180
8060 200
8070 220
Under Development
8005 113 < 0,07 13 2.7 2.8 3.4 215 186

 

Packaging

Packing ID Bags/Sacks Pallet
  Dimensions (mmxmmxmm) Net Weight (kg) LxW               (mmxmm) Number/ Pallet
Sacks 810x390x120 700 1200x800 28
Big Bags 910x910x1650 950-1000 1000x1000 1
Octabins 1105x1105x1750 950 1400x1400 1

Note: Non-standard packaging is subject to special agreement

Yarns for Ropes & Nets

High and Super High Tenacity, Multifilament Polyamide 6 (White & Spun-dyed) Yarns for the Specialty & Industrial Ropes and Nets Markets:

- Climbing & Playground Ropes

- Paper Carrier Ropes

- Fish Netting

- Fish Farming Nets

- Sport & Safety Nets

Yarns for airbags & weaving applications

High and Super High Tenacity, Multifilament Polyamide 6 (White & Spun-dyed) and 6.6 Yarns for Airbag and Weaving Markets:
- Airbag
- Broad Wovens
- Narrow Wovens
- Sewing Threads
- Air Jet Textured Applications

Yarns for tyres & MRG

High and Super High Tenacity, Multifilament Polyamide 6 and 6.6 Yarns for the Tyre and Mechanical Rubber Goods Markets:
- Passenger Car Tyres
- Off-Road Tyres
- Aircraft Tyres
- Conveyor Belts
- Airsprings
- Hoses

Special polymers

Polyamide 6.10, 6.12 (various viscosities) and PA6.6 Post-Condensation for Demanding Monofilament and Other Applications:
- Monofilaments
- Engineering Plastics
- Filtrations
- Abrasives

Twisted & Air-Jet Textured Yarns

Twisted and Air-Jet Texturing using Polyamide or your own yarn (PES, Acetate, Viscose, etc.) for Industrial Applications:

- Ropes and Nets Pre-Twisted Yarns

- Chafer for Tyres and Textile Applications

- Fancy Yarns

CREATING THE NEXT GENERATION OF YARNS AND FIBERS